Our PENGUEN SERIES waterproofing membranes are the plastomeric waterproofing membranes that are the ideal preference in the temperate zone. In our membranes, atacticpolypropylene (APP) with thermoplastic resin is used to increase the resistance of bitumen. And glass fiber-matte or polyester felt mat is used as load-bearer to increase the physical strength of the membranes. Meltdown and leaking under hot weather conditions, or cracking and breaking under cold weather conditions are not concerned. It is easy to apply with Blowpipe flame; it is cost-effective; and it has won the insulation masters' approval with this feature.
Application Areas: it is used on terrace and tilted reinforced concrete roofs in basic tanking and basic curtaining, and in waterproofing of wet and watery floors.
Cold brittleness: -5°C
Softening point: 130°C
Breakpoint: -14°C
| TECHNICAL FEATURES OF STANDART PENGUEN SERIES |
| Attribute |
STANDART |
UNIT |
PENGUEN |
PENGUEN |
PENGUEN |
PENGUEN |
PENGUEN |
PENGUEN |
PENGUEN |
| Reinforcement |
|
|
Glas tissue |
Glas tissue |
S.polyestermat |
S.polyestermat |
Glas tissue |
S.polyestermat |
S.polyestermat |
| Reinforcement Weight |
TS 11758 |
g / m² |
50 |
50 |
170 |
170 |
50 |
170 |
170 |
| Thickness |
TS 11758 |
mm |
2 |
3 |
3 |
4 |
3 |
3 |
4 |
| Weight |
TS 11758 |
kg / m² |
2,2 |
3,2 |
3,2 |
4,2 |
3,2 |
3,2 |
4,2 |
| Width |
TS 11758 |
m |
1 |
1 |
1 |
1 |
1 |
1 |
1 |
| Length |
TS 11758 |
m |
10 |
10 |
10 |
10 |
10 |
10 |
10 |
| Softening Point |
TS 120 |
C |
130 |
130 |
130 |
130 |
130 |
130 |
130 |
| Penetration (25 Cº ) |
TS 118 |
dmm |
20-30 |
20-30 |
20-30 |
20-30 |
20-30 |
20-30 |
20-30 |
| Cold Flexibility |
TS 11758 |
C |
-5 |
-5 |
-5 |
-5 |
-5 |
-5 |
-5 |
| Breaking at cold fraass |
TS 11758 |
C |
-14 |
-14 |
-14 |
-14 |
-14 |
-14 |
-14 |
| Water Impermeability |
TS 11758 |
_ |
* |
* |
* |
* |
* |
* |
* |
| Tensile strenght ( least ) |
TS 1908 |
N/5cm |
320 |
320 |
610 |
610 |
320 |
610 |
610 |
| Tensile strenght ( least ) |
TS 1908 |
N/5cm |
220 |
220 |
410 |
410 |
220 |
410 |
410 |
| Elongation at break |
TS 1908 |
% |
2 |
2 |
35 |
35 |
2 |
35 |
35 |
| Elongation at break |
TS 1908 |
% |
2 |
2 |
35 |
35 |
2 |
35 |
35 |
| Upper surface |
_ |
_ |
PE FİLM |
PE FİLM |
PE FİLM |
PE FİLM |
Al foil |
Al foil |
Al foil |
| Lower surface |
_ |
_ |
PE FİLM |
PE FİLM |
PE FİLM |
PE FİLM |
PE FİLM |
PE FİLM |
PE FİLM |
|
|